THE IMPORTANCE AND CHEMICAL-MINERALOGICAL ANALYSIS OF "OSMONSOY" HEMATITE IN OBTAINING PIGMENT
Jamoliddin Khonimkulov
Student (PhD)
Institute of General and Inorganic Chemistry of the Academy of Sciences of the Republic of Uzbekistan, Republic of Uzbekistan, Tashkent E-mail: [email protected]
Zulayho Kadyrova
Doctor of Chemical Sciences, Professor, Institute of General and Inorganic Chemistry of the Academy of Sciences of the Republic of Uzbekistan, Republic of Uzbekistan, Tashkent
ЗНАЧЕНИЕ И ХИМИКО-МИНЕРАЛОГИЧЕСКИЙ АНАЛИЗ ГЕМАТИТА «ОСМОНСОЙ»
В ПОЛУЧЕНИИ ПИГМЕНТА
Хонимкулов Жамолиддин Асатулла угли
докторант(PhD), Институт общей и неорганической химии Академии наук Республики Узбекистан, Республики Узбекистан, г. Ташкент
Кадырова Зулайхо Раимовна
д-р хим. наук, проф., Институт общей и неорганической химии Академии наук Республики Узбекистан, Республика Узбекистан, г. Ташкент
ABSTRACT
This work involved research on hematite ore, a local natural mineral raw material that could be used in the production of ceramic pigment. The article focuses on the chemical-mineralogical state of hematite ore present in the Jizzakh region. Results of spectral analysis, X-ray diffraction analysis have been cited and studied. Based on the results of the analysis, it was argued that the ore content of "Osmonsoy" hematite was sufficient to contain iron (III) oxide (Fe2O3), and its use in pigment synthesis could be promising.
АННОТАЦИЯ
Данная работа включала исследование гематитовой руды, местного природного минерального сырья, которое может быть использовано для производства керамического пигмента. В статье рассматривается химико-минералогическое состояние гематитовой руды, добываемой в Джизакской области. Приведены и изучены результаты спектрального анализа, рентгеноструктурного анализа. На основании результатов анализа было высказано предположение, что содержание гематита "Осмонсой" в руде было достаточным для содержания оксида железа (Ш) (Fe2O3), и его использование в синтезе пигментов может быть перспективным.
Keywords: Ceramic pigment, hematite, spectral analysis, maghemite, amorphous silica.
Ключевые слова: керамический пигмент, гематит, спектральный анализ, маггемит, аморфный кремнезем.
1. Introduction. In the production of ceramic products on an industrial scale, many natural and synthetic pigments are of great practical importance as coloring agents for glass, enamel and unglazed products. Currently, many ceramic inorganic pigments are being prepared and have a wide range of applications, in particular, they are one of the necessary components for the production of traditional glazed and unglazed tiles.
When inorganic pigments are used for colored ceramic products, certain conditions are required[1-3], in particular, the pigment must be thermally stable to the firing temperature[4]. Among the synthetic inorganic ceramic pigments used in the ceramic industry, there is a limited selection for red-pink and orange colors (Cr-Sn-Ca-Si, Pb-Sb-Sn-Fe, Mn-Al systems). They are generally easy to work with when glass is being processed,
Библиографическое описание: Khonimkulov J., Kadyrova Z. THE IMPORTANCE AND CHEMICAL-MINERALOGICAL ANALYSIS OF "OSMONSOY' HEMATITE IN OBTAINING PIGMENT // Universum: технические науки : электрон. научн. журн. 2024. 6(123). URL: https://7universum.com/ru/tech/archive/item/17789
№ 6(123)
but can be sensitive to the atmosphere and high temperatures.
In recent years, interest in inclusive pigments has been developing. The main reason for this is that it makes coloring substances resistant to heat and chemical conditions in industry by introducing them into a stable vitreous or crystalline Matrix (heteromorph pigments) [4-6].
There has been much research on Iron (III) oxide. Iron (III) oxide (Fe2O3) has four polymorphic forms: a-Fe2O3, P-Fe2O3, y-Fe2O3, and e-Fe2O3[6]. Of particular
июнь, 2024 г.
importance among them are the forms a-Fe2O3 (hematite) and y-Fe2O3 (maggemite).
Hematite occurs naturally as a crystalline mineral composed of Iron (III) oxide. It was also used by humans as a color pigment (red ocher) in burials dating to the Upper Paleolithic about 14,000 years ago[7-9]. They are often called ocher and have been used to discuss the antiquity of human symbolic behavior and for artistic purposes[10-15] it is found in sandstone, granite, quartzite or various metamorphic rocks. It is red in powder state as a pigment, but may vary in color when found in nature[16] Figure 1.
c d
Figure 1. Examples of Osmonsoy hematite. a, b) large samples c) granule d) powder state
Hematite is a cheap and low energy material in obtaining pigment [17-19]. In industry, large pieces are used mainly for the production of steel. Small pieces are used to obtain pigment in powder state. Samples of osmotic hematite X-ray diffraction results showed that there are sources of high-quality hematite in the Jizzakh region and that it is relevant to carry out studies to establish and improve the use of this material. One possible improvement is to increase the use of this material by establishing the production of pigments, which is due to the high demand for ceramic pigments and the relatively expensive cost.
The extraction of existing hematite raw material ores in the Jizzakh region is promising in obtaining pigment, and the chemical composition of the ore is mentioned in Table 1.
2. Research materials and methods
The materials used in this research work are hematite from the "Osmonsoy" mine, limestone (CaCO3), SiO2 * nH2O or microsilica (SiO2) from Uzmetkombinat waste, boron oxide (B2O3).
When the physico-chemical properties of raw materials and minerals in this area are studied by X-ray phase and spectral analysis methods, it can be seen that they are sufficiently saturated with iron (III) oxide for the production of red ceramic pigment.
№ 6(123)
HMHb, 2024 r.
Chemical composition of the mineral hematite Osmonsoy mine
Table 1.
Raw material Oxide composition, mass. %
Fe2O3 SiO2 CaO MgO AhO3
Hematite 60.80 25.40 7.30 2.79 2.60
Figure 2. Spectral analysis of hematite ore
Preparation of samples. The hematite mineral was ground to a size of 0.1 mm in a ball mill. The oxides of limestone, SiO2 * nH2O and amorphous silicon (iv) were ground separately. The components were pulled in proper proportions, and the samples were prepared at 900-1300° C by the traditional cooking method in an electric oven for 240 minutes (heating and cooling rate 20°C/min). Ready-state SiO2 * nH2O or amorphous silicon ( iv ) oxide is used in order to accelerate reaction progress and increase surface area. For the purpose of tempering, B2O3 was added to the mass in an amount of 2%. The temperature was systematically raised and proportionally lowered [20].
X-ray diffraction lines were obtained using the traditional powder method in Cu Ka-filter radiation (X = 0.154 nm) to determine the crystalline phases present in raw and matured samples.
X-ray diffraction patterns of pigments show that with an increase in the content of chromophores in pigments, the intensity of diffraction reflections decreases. This is due to a violation of symmetry and a violation of the crystal lattice when introducing coloring ions into the structure and the formation of solid solutions.
Figure 3. X-ray image of the hematite mineral from the Osmonsoy mine
№ 6(123)
июнь, 2024 г.
Figure 4. X-ray images of 3CaO*FeO3*3SiO2 ceramic pigments at different temperatures: 1000°C (A) and 1100°C (B)
3. Discussion. An X-ray of the mineral Osmonsoy hematite shows the presence of oxides Si, Fe, Al, Ca, Mg, and they are of sufficient composition in pigment synthesis. Samples cooked at different temperatures can be seen to produce mineral phases from X-ray diffraction maximums such as andradit, vallostanite, cristobalite, which imposes a color characteristic on the pigment.
Conclusion. In summary, pigments based on hematite (3CaO*Fe2O3*3SiO2) were successfully prepared using a solid-state reaction method, derived from an Uz-metkombinat waste as a Silicon source, and a calcium source from limestone and using the mineral hematite.
The resulting red pigment is suitable for painting ceramic tiles. However, the presence of impurities in the composition, the color intensity is not as strong as pigments, which are usually made with high purity oxides. Nevertheless, in terms of practical importance, the red color of the pigment obtained from industrial waste has a good effect compared to the pigment obtained from pure oxides. The results of the analysis showed that the synthesized pigments have good chemical and thermal stability at high temperatures. This work proved that it was possible to obtain a promising calculated ceramic pigment based on waste and local raw materials.
References:
1. A. Pal, A.N. Samanta, S. Ray, Treatment of iron ore slime for value addition, Hydrometallurgy 105 (2010) 30-35.
2. Dondi, M., & Eppler, R.A. (2000). Ceramic colorants. Ullmann's Encyclopedia of Industrial Chemistry, 1-18.
3. Dondi, M., Raimondo, M., & Zanelli, C. (2014). Clays and bodies for ceramic tiles: Reappraisal and technological classification. Applied Clay Science, 96, 91-109.
4. Масленникова Г.Н., Пищ И.В., Керамические пигменты, Москва, Стройматериалы, 2009, 220 с.
5. F.Bondioli,A.M.Ferrari, C.Leonelli,T.Manfredini; Mater.Res.Bull., 33(5), 723-9.
6. F.Bondioli,T.Manfredini, C.Siligardi,A.M.Ferrari; Journal of the American Ceramic Society, 88(4), 1070
7. M.Hosseini Zori, E.Taheri,A.R.Mirhabibi; Ceram. Int., 34, 491-496.
8. C. Li, H. Sun, J. Bai, L. Li, Innovative methodology for comprehensive utilization of iron ore tailings: Part 1. The recovery of iron from iron ore tailings using magnetic separation after magnetizing roasting, J. Hazard. Mater. 174 (2010) 71-77.
9. C. Li, H. Sun, Z. Yi, L. Li, Innovative methodology for comprehensive utilization of iron ore tailings: Part 2. The residues after iron recovery from iron ore tailings to prepare cementitious material, J. Hazard. Mater. 174 (2010) 78-83.
10. Vicent JB, Llusar M, Badenes J, Tena MA, Vicente M, Monros G. Occlusion of chromophore oxides by solegel methods: application to the synthesis of hematiteesilica red pigments.Bol Soc EspCeram Vidrio 2000;39(1):83e93
11. Bondioli F, Ferrari AM, Leonelli C, Manfredini T. Synthesis of Fe2O3/ silica red inorganic inclusion pigments for ceramic application. Mater Res Bull 1998;33(5):723e9
12. Llusar M, Badenes JA, Calbo J, Tena MA, Monros G. Environmental and colour optimisation of mineraliser addition in synthesis of iron zircon ceramic pigment. Br Ceram Trans 2000;99(1):14e22
13. Katsuki H, Komarneni S. Role of a-Fe2O3 morphology on the color of red pigment for porcelain. J Am Ceram Soc 2003, 86: 183-185.
14. Gualtieri AF. Natural red pigment for single-fired ceramic glaze. Ceram Bull 2002, 81: 48-52.
15. W. Hajjaji, M.P. Seabra, J.A. Labrincha, J. Hazard. Mater. 185, 619-625 (2011).
16. V.M. Beleza, R.A. Boaventura, M.F. Almeida, Environ. Sci. Technol. 35, 4379-4383 (2001).
17. M. Erdem, J. Hazard. Mater. 129, 143-146 (2006).
18. L.J. Lozano, D. Juan, Miner. Eng. 14, 543-546 (2001).
19. S. Vitolo, M. Seggiani, S. Filippi, C. Brocchini, Hydrometallurgy 57, 141-149 (2000).
20. H. Yungevis, E. Ozel, Ceram. Int. 39, 5503-5511 (2013).