Synthesis and Characterization of Natural Sensitizers for Dye Sensitized Solar Cells
Mohammed Isah Kimpa 1, Kasim Uthman Isah 1, Jibrin Alhaji Yabagi 2, Sulaiman Taufiq 3, Mohd Arif Bin Agam 4
1 Federal University of Technology Minna P. M. B. 65, Minna, Nigeria
2 Ibrahim Badamasi Babangida University Lapai KM3, Minna Road, Lapai, Nigeria
3 Umaru Waziri Federal Polytechnics P. M. B. 1034, Birnin Kebbi, Nigeria
4 Universiti Tun Hussein Onn Malaysia
101 Beg Berkunci, Parit Raja, Batu Pahat, Johor, 86400, Malaysia
Abstract. Natural dyes of anthocyanin extract from flame tree flower (Delonix regia) and chlorophyll extract from pawpaw leaf (Carica papaya) were used as sensitizer to fabricate dye sensitized solar cell (DSSC). The photoelectrode were subjected to UV/Vis spectrophotometer to view their absorbability. The photo electrochemical performances of DSSCs obtained from I.V characteristics showed conversion efficiency, (q) of 0.80 % for the dye extracts from flame tree flower (anthocyanine), with open-circuit voltage (VOC) of 0.5249 mV, short-circuit current density (Isc) of 44.6191 mA/m2 and Fill factor (FF) of 0.5837. Chlorophyll dyes extract from pawpaw leaf has VOC, Isc, FF and conversion efficiency, (q) of 0.5249 mV, 16.5283 mA/m2, 0.5585 and 0.27 % respectively. The conversion efficiency for the mixed dyes (anthocyanin and chlorophyll) at ratio 1:2 is 0.23 % with VOC, Isc and FF of 0.5500 mV, 14.2750 mA/m2 and 0.5451 respectively, while the dye mixture at ratio 1:4 achieved VOC of 0.5249 mV, Isc of 18.4941 mA/m2, FF of 0.5206 and conversion efficiency (q) of 0.26 %. Anthocyanine from flame tree flower dye extract had the higher conversion efficiency of 0.8 % which could be better in term of application in dye solar cell.
Keywords: flame tree flower; pawpaw leaf; solar cell; absorbance; chlorophyll; anthocyanin.
DOI: 10.22178/pos.27-3
LCC Subject Category: TP155-156, QC450-467, QD450-801
Received 15.09.2017 Accepted 18.10.2017 Published online 20.10.2017
Corresponding Author: kimpa@futminna.edu.ng
© 2017 The Authors. This article is licensed under a Creative Commons Attribution 4.0 License
INTRODUCTION
Dye-sensitized solar cell (DSSC) is a device that change light into electric energy by light sensiti-zation established on wide energy-band semiconductor [1]. Conventionally, solar cells semiconductor has the task of light absorption and the transportation of charge-carrier, whereby in the DSSCs, they are separately controlled [2]. The photosensitizing dye adsorbed on the nano-crystalline TiO2 semiconductor, absorbs light. The ejected electrons excite to the conduction band of the semiconductor leaving the oxidized dye molecules behind [3]. The electrons travel to the counter electrode through the external circuit to reduce the iodide ion of the electrolyte. The iodide ions transport the electrons back to the dye [4].
Among the dye-sensitized solar cells, the dye-sensitized solar cell using Ruthenium complex shows a high conversion efficiency of about 1112 % [5]. However, Ruthenium is a rare metal and the cost of ruthenium complex is very high. On the other hand natural dye is easy to obtain and the cost is very low [6]. Green plants are mostly rich in chlorophyll and red leaves are rich in anthocyanine [7] and the application of this kind of natural dye has been frequently investigated in many related studies [3, 8, 9].
In this paper, extracts of pawpaw leaves and flame tree flower were the natural dyes used as light sensitizers for the preparation of DSSCs. The conversion efficiency of the DSSCs was investigated via solar simulator.
MATERIAL AND METHODS Preparation of natural dye
Fresh pawpaw leaves and flame tree flower were separately squeezed to obtained a pure and natural dye solution. Water was used as the extracting solvent. The extract fluid were heated separately for 10 min to extract chlorophyll from pawpaw leave dye solution and anthocyanine from flame tree flower dye solution. Then, the extract solution of pawpaw leaves and flame tree flower were blended at the ratios of 1:2 and 1:4 to serve as natural dye cocktail from these two plants.
Preparation of the TiO2/Dye Electrode
The ITO glass (0.03 cm*0.7 cm=0.021 cm2) was cleaned with distilled water and acetone to remove impurities. The cleaned ITO surface was coated with commercially available nanocrystal-line TiO2 paste using the screen printing method. To improve this situation and increase the compactness of thin film, the ITO/TiO2 electrodes were sintered at 450 °C for 1 hour. When the temperature of the TiO2 electrodes reached 80 °C during cooling, the electrodes were immersed into different dyes solution for 24 hours. The white TiO2 film will change color when dye is adsorbed on the TiO2 electrode. The TiO2/dye electrode was washed with water and ethanol to remove impurities and trapped water. After cleaning, the DSSCs photoelectrode was complete and ready for testing.
of the cell was completely wetted with the electrolyte. The cell was now complete and operational. Schematic diagram of the molecular structure of the anthocyanine obtained from the red leaf extract of Flame tree flower is shown in Figure 1(a) and 1(b).
A
ho-/ \ OH
/ ^OH
CH2 \
OH
OH
OH
B
OH
Figure 1-Chemical structure of anthocyanin (a) - Cyanidine 3-O-rutinoside and (b) - Cyanidine 3-O-glucoside
The assembly of DSSCs
DSSCs were encapsulated according to the general assembly procedures [10]. A DSSC is mainly comprised of ITO conductive glass, TiO2 nanopar-ticles, natural dye, an electrolyte, counter electrode and spacers. A glass insulation spacer in long strips was initially stuck on the four edges on the base plate of conductive glass at the bottom to create space between photoelectrode and counter electrode and enabling the injection of electrolyte after assembly. AB glue was used to bind the base plate of lower conductive glass carrying the counter electrode with the base plate of upper conductive glass carrying the photoelec-trode. The gap between the electrodes was filled with the electrolyte to make the cell complete. This was performed by capillary effect. The process was repeated until the entire internal surface
Measurement of photoelectric conversion efficiency of DSSC
The photoelectric conversion efficiency of DSSC was inspected under the simulated sunlight source (A.M 1.5) with current - voltage (I-V) characteristic, the fill-factor (FF) was defined as (1):
I x V
J7J7 _ max max
Isc x Voc
(1)
where denote maximum output
value of current and voltage respectively, and denote the short circuit current and open-circuit voltage respectively. The total energy conversion efficiency was defined as (2):
1 =
Isc * Voc * FF
(2)
where Pin denotes the energy of incident photon.
The paste was observed to have agglomeration particle size with film porosity which allows electrons to travel and be collected at the surface of the conduction substrate. Figure 4 show the analysis of the elemental composition of TiO2 anatase.
RESULTS AND DISCUSSION XRD and SEM analysis
Figure 2 shows the XRD pattern of the TiO2 nano-particle. The spectrum is identical to the standard data sheet (JCPD 01-075-8897).
Figure 2 - XRD analysis of the anatase TiO2 thin film
The XRD pattern observed in this study is in agreement with previous report [8]. Surface morphology of the TiO2 nanocrystalline is presented in Figure 3, which shows homogeneous and uniform spread of the anatase TiO2 film on the glass substrate.
Mag = 83.04 KX
Figure 3 - SEM image of the photo electrode thin film fabricated using screen printing method
Spectrum 1
0 ii 1.........a.......k.
jb 4 6 8 10 12' 14 :ull Scale 30970 cts CursorfO.OOO_keV
Figure 4 - EDX image of the photo electrode of TiO2
The analysis revealed the presence of titanium, oxygen and very little chlorine. Chlorine was detected in the compound due to TiCU that contained in the preparation of anatase TiO2 compound. For any efficient solar cell, the EDX revealed the compound composition of the element it's composed.
Any other element found outside the TiO2 semiconductor compound could degrade the performance of the solar cell.
Absorption of natural dyes
Figure 5 show the absorption spectra of the pawpaw leaf extracts, mixed dye extracts of pawpaw and flame tree flower at ratio 1:2 and 1:4. The absorption spectrum for the three dyes extract where within the wavelength of 300 to 550 nm with the maximum peak absorption value at 380 nm for mixed dyes at 1:4. The difference in absorption peak for different dye extract could be as a result of differences in chemical structure of these pigments.
Figure 6 show the absorption spectra of the flame tree flower and mixed dye extracts at the ratio of 1:2 and 1:4. Figure 7 depict the absorption spectra from the extracts of flame tree flower, pawpaw leaf, mixed dyes at 1:4 and 1:2. It was observed in (Figure 6 & 7) that the absorption range of the dye extracts is between 300550 nm with absorption peak at wavelength of 380 nm for the dye cocktail (mixed dye) at ratio
(1:2 and 1:4) and flame tree flower while the absorption peak of pawpaw leaf extracts was at 350 nm.
Figure 5 - Absorption spectra of mixed dye extracts at 1:4, pawpaw dye and mixed dye at 1:2
All the absorption spectrum (Figures 5-7) shows the absorption of the dye extracts within the Ultra-Violet Visible range with the absorption peak at the violet color region that appears green-yellow color as complementary color. Pawpaw leaf dye extracts absorbed light at lower peak than other dye extracts. This could be as a result of the extracting solvent use in this study. Similar work was done by [7] with ethanol as the extracting solvent and pawpaw leaf extract had better absorption peak than flame tree flower extract. Another reason that could lower the absorption peak of pawpaw extract among the study dyes could be due to different absorption properties for different pigments and colors of different extract fluids [8].
Figure 8 shows the photovoltaic test of DSSCs using these natural dyes as sensitizers.
Figure 6 - Absorption spectra of the mixed dyes extracts at 1:2, 1:4 and flame tree flower extracts
Figure 8 - I-V Characteristic of DSSC sensitized by natural dye extracts from pawpaw leaf, flame flower leaf, mixed dyes at 1:2 and 1:4
Figure 7 - Absorption spectra of the mixed dye extracts at ratio 1:2, 1:4, pawpaw leaf extract and flame tree flower extracts of DSSC
Their performances were measured by current-voltage (I-V) curves under irradiation with halogen lamp (100 mWcm-2) from solar simulator. Table 1 shows the data acquired from measuring the photoelectric conversion efficiency of the DSSCs.
Table 1 - Photo electrochemical parameters of the DSSCs sensitized by natural dyes extracted with
water in the UV-vis ight range
Dye Voc, mV Isc, mAcm-2 FF n, %
Flame tree flower 0.5249 44.6191 0.5837 0.80
Pawpaw leaf 0.5249 16.5283 0.5585 0.27
Mixed dye 1:4 0.5249 18.4941 0.5206 0.26
Mixed dye 1:2 0.5500 14.2750 0.5451 0.23
From the results obtained, natural dye extracts from flame tree flower had the highest conversion efficiency than pawpaw leaf dye extracts and the cocktail dye extracts that were blended in two different ratios (1:2 and 1:4). This could be as a result of the chlorophyll extracts from pawpaw leaf and the extracting solvent (water). More also the blended ratio could also be the reason for their lower efficiencies because the antho-cyanine dye extracts from flame tree flower that shows the highest conversion efficiency was the dye extracts that was added to the chlorophyll dye extracts at different ratio, chlorophyll was kept constant. Another reason for their lower efficiencies could also be from their absorbability capacity.
Furthermore, Table 1 compares different property parameters of DSSCs using different natural dyes, including short-circuit photo current density (Jsc), open-circuit voltage (Voc), fill factor (FF) and energy conversion efficiency (n). As shown in Table 1, the photoelectric conversion efficiency of flame tree flower extract fluid is higher than the photoelectric conversion efficiency of the extracts from pawpaw leaf and the dye mixtures at ratio 1:2 and 1:4. This is because the absorption intensity of flame tree flower is higher than the other dye extracts. In addition, DSSCs fabricated from the extracts of flame tree flower had better charge-transfer performance and clearly improved efficiency to 0.8 %. Figure 9 shows the power against voltage curves of the DSSCs using the natural dyes extracted from the pawpaw leaf, flame tree flower, mixed dye at ratio 1:2 and 1:4.
The DSSC using natural dye extracts from flame tree flower has the maximum power rate of about 13.6704 mW.
Figure 9 - Plot of power against voltage for DSSC sensitized by natural dyes extracts from pawpaw leaf, flame tree flower, mixed dyes at ratio 1:2 and 1:4
CONCLUSION
The measurement and analysis of the absorption spectra for natural dyes extracted from the pawpaw leaf, flame tree flower, mixed dye at 1:2 and 1:4 are carried out. The results show that the dye extracted from the flame tree flower has similar absorption spectrum to the dye extracts for the pawpaw leaf and their mixed dyes which has absorption wave band at 300-550 nm. The DSSC using the flame tree flower dye extracts has the best photo electric conversion efficiency of 0.80 % and has the maximum power of about 13.6704 mW.
ACKNOWLEDGMENT
The authors would like to thank the entire staff of the Physics Advanced Lab, Sheda Science and Technology Complex (SHESTCO) Abuja for allowing us to use their laboratory.
REFERENCES
1. Chang, H., Kao, M.-J., Chen, T.-L., Kuo, C.-G., Cho, K.-C., & Lin, X.-P. (2010). Natural Sensitizer for Dye-
Sensitized Solar Cells Using Three Layers of Photoelectrode Thin Films with a Schottky Barrier. American Journal of Nanotechnology, 1(1), 13-22. doi: 10.3844/ajnsp.2010.13.22
2. Osman, U. M., Farizal, A. S. N., Razali, M. H., & Salleh, H. (2017). Synthesis of Nano Crystalline 1-[2-
(Trifluoro-Methyl) Benzylidene] Thiosemicarbazide with D-n-A Architecture towards Dyes Sensitized Solar Cells. Journal of Engineering and Applied Sciences, 12(9), 2506-2511.
3. Isah, K. U., Ahmadu, U., Idris, A., Kimpa, M. I., Uno, U. E., Ndamitso, M. M., & Alu, N. (2014). Betalain
pigments as natural photosensitizers for dye-sensitized solar cells: the effect of dye pH on the photoelectric parameters. Materials for Renewable and Sustainable Energy, 4(1). doi: 10.1007/s40243-014-0039-0
4. Pradhan, B., Batabyal, S. K., & Pal, A. J. (2007). Vertically aligned ZnO nanowire arrays in Rose Bengal-
based dye-sensitized solar cells. Solar Energy Materials and Solar Cells, 91(9), 769-773. doi: 10.1016/j.solmat.2007.01.006
5. Zhou, H., Wu, L., Gao, Y., & Ma, T. (2011). Dye-sensitized solar cells using 20 natural dyes as
sensitizers. Journal of Photochemistry and Photobiology A: Chemistry, 219(2-3), 188-194. doi: 10.1016/j.jphotochem.2011.02.008
6. Furukawa, S., Iino, H., Iwamoto, T., Kukita, K., & Yamauchi, S. (2009). Characteristics of dye-sensitized
solar cells using natural dye. Thin Solid Films, 518(2), 526-529. doi: 10.1016/j.tsf.2009.07.045
7. Isah Kimpa, M., Momoh, M., Uthman Isah, K., Nawawi Yahya, H., & Muhammed Ndamitso, M. (2012).
Photoelectric Characterization of Dye Sensitized Solar Cells Using Natural Dye from Pawpaw Leaf and Flame Tree Flower as Sensitizers. Materials Sciences and Applications, 03(05), 281-286. doi: 10.4236/msa.2012.35041
8. Chang, H., Wu, H. M., Chen, T. L., Huang, K. D., Jwo, C. S., & Lo, Y. J. (2010). Dye-sensitized solar cell
using natural dyes extracted from spinach and ipomoea. Journal of Alloys and Compounds, 495(2), 606-610. doi: 10.1016/j.jallcom.2009.10.057
9. Nair, G., Ramli, S., Irwanto, M., Yusoff, M. I., Fitra, M., Hashim, U., & Mariun, N. (2014). Fabrication of
Organic Dye Sensitized Solar Cell. Applied Mechanics and Materials, 699, 516-521. doi: 10.4028/www.scientific.net/amm.699.516
10. Kimpa, M. I. (2012). Fabrication and Analysis of Dye-Sensitized Solar Cells Using Natural Dyes
Extracted from Pawpaw Leaf and Flame Tree Flower and their Synthetic Ruthenium Dye (Master's Degree Dissertation). Sokoto: Usmanu Danfodiyo University Sokoto.