HIGH-MOLECULAR CONNECTIONS
DOI: 10.32 743/UniChem.2021.86.8.12068 SWELLING OF HYDROLYZED FIBROIN IN WATER, ACIDIC AND ALKALINE SOLUTIONS
Khushnudbek Eshchanov
Lecturer at the Department of Chemistry, Faculty of Natural Sciences,
Urgench State University, Uzbekistan, Urgench E-mail: olmos_77@mail.ru
Muhabbat Baltayeva
Associate Professor at the Department of Chemistry, Faculty of Natural Sciences,
Urgench State University, Uzbekistan, Urgench E-mail: bmuhabbat@rambler.ru
Abdushkur Sarimsakov
Institute of Chemistry and Polymer Physics of the Republican Academy of Sciences,
Deputy Director for Research, Uzbekistan, Tashkent E-mail: sarimsakov1948@mail.ru
Mekhriniso Sabirova
Student of chemistry, Urgench State University, Faculty of Natural Sciences,
Uzbekistan, Urgench E-mail: saburovamexriniso@gmail.com
НАБУХАНИЕ ГИДРОЛИЗОВАННОГО ФИБРОИНА В ВОДЕ, КИСЛОТНЫХ
И ЩЕЛОЧНЫХ РАСТВОРАХ
Эшчанов Хушнудбек Одилбекович
преп. кафедры химии естественного факультета Ургенчского государственного университета, Узбекистан, г. Ургенч E-mail: olmos_77@mail.ru
Балтаева Мухаббат Матназаровна
доцент кафедры химии естествознания Ургенчского государственного университета, Узбекистан, г. Ургенч E-mail: bmuhabbat@rambler.ru
Саримсаков Абдушкур Абдухалилович
заместитель директора по научной работе, Институт химии и физики полимеров РАН, Узбекистан, г. Ташкент E-mail: sarimsakov1948@mail.ru
Сабирова Мехринисо
студент, Ургенчский государственный университет, факультет естественных наук, кафедра химия,
Узбекистан, г. Ургенч E-mail: saburovamexriniso@gmail.com
Библиографическое описание : Swelling of hydrolyzed fibroin in water, acidic and alkaline solutions // Universum: химия и биология : электрон. научн. журн. Eshchanov K.O. [и др.]. 2021. 8(86). URL:
https://7universum.com/ru/nature/archive/item/12068
Д UNIVERSUM:
№ 8 (86)_химия и биология_июль, 2021 г.
ABSTRACT
This article provides information on the swelling of hydrolyzed fibroin derived from natural silk fibroin in water, acids and alkalis. The swelling properties of hydrolyzed fibroin derived from natural silk fibroin in different media were studied. Swelling levels of hydrolyzed fibroin were studied by observation on a swell meter and an optical microscope. As a result of the research, we found that the results obtained in both methods differed sharply from each other and studied its causes.
АННОТАЦИЯ
В этой статье представлена информация о набухании гидролизованного фиброина, полученного из натурального фиброина шелка, в воде, кислотах и щелочах. Изучены набухающие свойства гидролизованного фиброина, полученного из натурального фиброина шелка, в различных средах. Уровни набухания гидролизованного фиброина изучали путем наблюдения с помощью набухометра и оптического микроскопа. В результате исследования мы обнаружили, что результаты, полученные обоими методами, резко отличаются друг от друга, и изучили его причины.
Keywords: silk fibroin, swelling, hydrolyzed fibroin ("HF"), optical microscope, amorphous part.
Ключевые слова: фиброин шелка, набухание, гидролизованный фиброин («ГФ»), оптический микроскоп, аморфная часть.
Introduction. 70-75% of natural silk fiber consists of fibroin protein. Silk fibroin consists of amorphous (a-structure) and crystalline (P-structure) parts. The study of the swelling levels of silk fibroin helps to draw definite conclusions about its interactions with solvents in determining its sorption properties [1] [2] [3].
Silk fibroin is insoluble in water. Silk fibroin is extracted by washing the silk fiber with water. Fibroin is insoluble in alcohol, ether, benzene, acetone, carbon (IV) sulfide, and other organic solvents. Salts of calcium, strontium, barium, which form a solution in a neutral medium, and hydrogen halide acids, Schweitzer reagent, form colloidal systems in alkaline solutions [4]. It is also soluble in concentrated ZnCl2 solution and ammonia solutions of nickel(II) hydroxide [5].
Fibroin can absorb moisture in water-resulting in a limited swelling of 30-40%. The moisture retention of pure fibroin is 1,2 % lower than that of silk. It was found that the swelling of silk fibroin in the water at a temperature of 18oC increased the cross-section of the fiber by 18,7 % and the length by 1,3 % [6][7]. In his research, S.Sommer found that the swelling of silk fiber in the water at a temperature of 20oC increases the length of the fiber by 1,3-1,7%, the cross-sectional area by 19-46 %, and the mass by 3 5-54%.
Amorphous parts of natural silk fibroin absorb 70% moisture, while crystalline parts absorb 30% moisture. In acids and especially alkaline solutions, fibroin swelling increases. The swelling of fibroins in alkalis can be irreversible. Swelling of silk fibroin in dilute solutions of NaCl and NaNO3 salts is observed as in water [8].
We formed powdered hydrolyzed fibroin ("HF") by hydrolyzing natural silk fibroin in a 3% hydrochloric acid solution [9][10]. We conducted studies to determine the degree of swelling of powdered "HF" under acidic conditions (3% hydrochloric acid), alkaline (3% KOH) conditions, and water.
Experimental section
Materials. Fibrous of silk (Cleaned of additives. Khorezmipagi LLC, Urgench, Uzbekistan), HCl (chemically pure) and potassium hydroxide was purchased from Chimreaktivinvest (Uzbekistan).
Instrumentation. Bidistilled water is obtained from the "GFL 2104 Double distillation water still" device (Germany), swell meter (Russia), optical microscope ("Optika_B-150 DBR").
Procedure
Detection of "HF" powder swelling with a swell meter. The swelling of the "HF" powder was detected on a swell meter. On the swell meter, we found that the swelling levels of "HF" powder change over time under acidic, alkaline conditions and in water. The experiments were performed at a temperature of 20oC for 192 h.
Swelling was determined using the following formula.
Vo-the initial volume of the polymer, V-the volume of the polymer at time-/.
Detection of "HF" swelling by optical microscopy. The swelling of "HF" particles was determined by optical microscopy using the Optika_B-150 DBR optical microscope in acidic, alkaline conditions and bidistilled water at a temperature of 20oC.
Analysis and results
Swelling results of "HF" powder detected on the swell meter. The swell meter found that the swelling levels of "HF" powder did not change after 192 hours. Measurements on the swell meter revealed that the "HF" powder had a swelling rate of 15% in water and 23 and 70% swelling levels in acidic and alkaline conditions, respectively (Figure 1). A high degree of swelling in an alkaline environment means that the number of crystalline particles decreases due to structural changes in the "HF" and the number of amorphous particles increases.
№ 8 (86)
uwRb, 2021 ¿.
Figure 1. Swelling (%) of "HF" powder in water, alkaline and acidic solutions 20oC
Swelling results of "HF" detected under an optical microscope. The cylindrical shape of the "HF" particle al-
lows precise calculations to be performed (Figure 2). Expressions (2) and (3) were used to calculate the volume of cylindrical particles.
(2) (3)
Figure 2. Determining the diameter and length of an "HF" particle
The time-dependent graph of the values of the swell levels determined by the optical microscopy method is shown below (Figure 3).
i-irMr'j(n(n'=tLjiijivo\orv-aocaoimoi-iiH
swelling in an alkaline environment
swelling in an acidic environment
swelling in a neutral environments the water}
Figure 3. Time dependence of "HF" particle swelling (%) in acidic, alkaline media and water as determined by
optical microscope (20°C)
№ 8 (86)
• 7universum.com
UNIVERSUM:
, XMMna M BM0/i0rMii
HM^b, 2021 r.
It can be seen that the differences between the degree of swelling of the individual "HF" particle detected by optical microscopy and the degree of swelling of the
"HF" powder detected on the swell meter are very large (Figure 4).
120
100 80
60 40
J r:
20
0 —*- — — — —♦- —
^ q^ ^ A^ ^ NT T? & V V" <bto
Figure 4. A) The time dependence of the swelling (%) of "HF" powder in water as determined by a swell meter at a temperature of 20°C. B) The time dependence of the swelling of "HF" particles in water detected by an optical
microscope at a temperature of 20oC
Figure 5. Time dependence of swelling (%) levels of "HF" powder and its particle in acidic environment (20oC)
• "HF" al ksline environ meritswelling of the powder (a] "HF" pa rticle swellingi n alkaline medium (a]
Figure 6. Time dependence of swelling (%) levels of "HF" powder and its particle in alkaline medium (20oC)
In the swell meter, an error occurs in determining the increase in total volume as a result of the increase in particle size during the swelling of the "HF", their friction against
the device wall, and the filling of the gaps between the particles.
№ 8 (86)
In optical microscopy, no external mechanical forces affect the swelling of "HF" particles. Therefore, it can be seen that the swelling detected by this method has a high value.
Conclusion. It can be said that the reason for the high value of "HF" swelling in an alkaline solution is due to changes in its composition and an increase in the number
июль, 2021 г.
of amorphous parts. Hence, in an alkaline environment, the number of crystalline parts of "HF" decreases and the number of amorphous parts increases. Since there is no external influence on the swelling of the "HF" particle detected by the optical microscope, it can be considered as absolutely true about the swelling levels of the "HF" powder detected in the swell meter.
References:
1. Yu.V.Brestkin "Dynamic coil-extended chain phase transition in the longitudinal field"//Acta Polymerica.-Berlin:, 1987. -№ 8 (38).- P. 470-477.
2. Mitsuru Sato, Katsura Kojima, Yasushi Tamada, Hiroshi Kitani. Production of scFv-conjugated"Affinity Silk" by transgenic silkworm technology. Japan-2012.-377.
3. Xinfang Liu, Ke-Qin Zhang, " Silk Fiber-Molecular Formation Mechanism, Structure-Property Relationship and Advanced Applications". //National Engineering Laboratory for Modern Silk, College of Textile and Clothing Engineering, Soochow University, Suzhou. China: Soochow University. 2014.
4. Б.Э.Геллер, А.А.Геллер, В.Г.Чиртулов "Практическое руководство по физикохимии волокнообразующих полимеров". Москва. 1996 -432с.
5. Натуральный и искусственный шелк/ Шелковные текстильные волокна и ткани. https://www.otkani.ru.
6. Г.Е.Кричевский, М.В.Корчагин, А.В.Сенахов. "Химическая технология текстильных материалов", Москва Легпромбытиздат 1985 г.
7. О.И.Одинцова, М.Н.Кротова, С.В.Смирнова, "Основы текстилново материаловедения", Иваново-2008. -36-37 c.
8. Ю.А.Москвтечев, В.Ш.Фельдблюм, Химиya в нашей жизни (продукты органического синтеза и их применение): Монография .-Ярославль: Изд-во ЯГТУ, 2007.-411 с.
9. Kh.O. Eshchanov, M.M. Baltayeva, A.A. Sarimsakov. (2021). Purification of Cottonseed Oil Using A Sorbent Obtained from the Fibrous Waste of Natural Silk. Annals of the Romanian Society for Cell Biology, 692-698. Retrieved from http://annalsofrscb.ro/index.php/journal/article/view/159
10. Эшчанов Хушнудбек Одилбекович, Шигабутдинов Амир Анварович. Изучения Процесса гидролиза фиброина и метода получения "Полимер-металл" комплексов. Инновационное развитие современной науки: проблемы, закономерности, перспективы: сборник статей IV Международной научно-практической конференции. В 2ч.Ч. 1.-Пенза: МЦНС «Наука и Просвещение». - 2017. -242 с.