Научная статья на тему 'STUDY OF OBTAINING ACCOMPANYING ELEMENTS IN THE PROCESSING OF GOLD-BEARING ORES OF THE MURUNTAU DEPOSIT'

STUDY OF OBTAINING ACCOMPANYING ELEMENTS IN THE PROCESSING OF GOLD-BEARING ORES OF THE MURUNTAU DEPOSIT Текст научной статьи по специальности «Биотехнологии в медицине»

CC BY
39
21
i Надоели баннеры? Вы всегда можете отключить рекламу.
Ключевые слова
EXTRACTION / PRECIPITATION / ZINC POWDER / ALUMINUM AND IRON CHIPS / ION EXCHANGE RESIN / SULFURIC ACID TREATMENT / NITRIC ACID TREATMENT

Аннотация научной статьи по биотехнологиям в медицине, автор научной работы — Polvanov Sardor, Ergashev Nurbek, Khodzhiev Murod, Tashmuratov Anvar

This article reflects the research conducted on the deposition of silver and other valuable metals from waste sulfuric acid solutions by cementation with zinc powder. The issue of nitric acid dissolution of the resulting precipitate after cementation with zinc powder, with further separation of silver and non-ferrous metals, is considered.

i Надоели баннеры? Вы всегда можете отключить рекламу.
iНе можете найти то, что вам нужно? Попробуйте сервис подбора литературы.
i Надоели баннеры? Вы всегда можете отключить рекламу.

Текст научной работы на тему «STUDY OF OBTAINING ACCOMPANYING ELEMENTS IN THE PROCESSING OF GOLD-BEARING ORES OF THE MURUNTAU DEPOSIT»

№ 7 (100)

A UNI

1Ш. ТЕ)

UNIVERSUM:

ТЕХНИЧЕСКИЕ НАУКИ

июль, 2022 г.

METALLURGY AND MATERIALS SCIENCE

DOI: 10.32743/UniTech.2022.100.7.14079

STUDY OF OBTAINING ACCOMPANYING ELEMENTS IN THE PROCESSING OF GOLD-BEARING ORES OF THE MURUNTAU DEPOSIT

Sardor Polvanov

Head of the sorption and regeneration shop of HMP-2 JSC NMMC, Republic of Uzbekistan, Navoi E-mail: sardor8 78 [email protected]

Nurbek Ergashev

Head of the central plant laboratory of HMP-2 JSC NMMC, Republic of Uzbekistan, Navoi E-mail: [email protected]

Murod Khodzhiev

Foreman (technologist) of the sorption and regeneration shop of HMP-2 JSC NMMC, Republic of Uzbekistan, Navoi E-mail: khodjiev. [email protected]

Anvar Tashmuratov

Operator

of the sorption and regeneration shop HMP-2 JSC NMMC

Republic of Uzbekistan, Navoi E-mail: [email protected]

ИССЛЕДОВАНИЕ ПОЛУЧЕНИЯ СОПУТСТВУЮЩИХ ЭЛЕМЕНТОВ ПРИ ПЕРЕРАБОТКЕ ЗОЛОТОСОДЕРЖАЩИХ РУД МЕСТОРОЖДЕНИЯ «МУРУНТАУ»

Полванов Сардор Комилович

начальник цеха сорбции и регенерации ГМЗ-2 АО НГМК, Республика Узбекистан, г. Навои

Эргашев Нурбек Улугбекович

начальник

центральной заводской лаборатории ГМЗ-2 АО НГМК, Республика Узбекистан, г. Навои

Ходжиев Мурод Шарафиддин угли

мастер (технолог) цеха сорбции и регенерации ГМЗ-2 АО НГМК, Республика Узбекистан, г. Навои

Ташмуратов Анвар Санакулович

аппаратчик

цеха сорбции и регенерации ГМЗ-2 АО НГМК, Республика Узбекистан, г. Навои

Библиографическое описание: STUDY OF OBTAINING ACCOMPANYING ELEMENTS IN THE PROCESSING OF GOLD-BEARING ORES OF THE MURUNTAU DEPOSIT // Universum: технические науки : электрон. научн. журн. Polvanov S.K. [и др.]. 2022. 7(100). URL: https://7universum. com/ru/tech/archive/item/14079

№ 7 (100)

UNIVERSUM:

ТЕХНИЧЕСКИЕ НАУКИ

июль, 2022 г.

ABSTRACT

This article reflects the research conducted on the deposition of silver and other valuable metals from waste sulfuric acid solutions by cementation with zinc powder. The issue of nitric acid dissolution of the resulting precipitate after cementation with zinc powder, with further separation of silver and non-ferrous metals, is considered.

АННОТАЦИЯ

В данной статье отражаются проведенные исследования по осаждению серебра и других ценных металлов из сбросных сернокислотных растворов путем цементации цинковым порошком. Рассмотрен вопрос азотнокислого растворения полученного осадка после цементации цинковым порошком, с дальнейшим разделением серебра и цветных металлов.

Keywords: extraction, precipitation, zinc powder, aluminum and iron chips, ion exchange resin, sulfuric acid treatment, nitric acid treatment.

Ключевые слова: извлечение, осаждение, цинковый порошок, алюминиевая и железная стружка, ионообменная смола, сернокислотная обработка, азотнокислотная обработка.

The hydrometallurgical plant No. 2 (HMP-2) of the Navoi Mining and Metallurgical Combine (Uzbekistan) processes gold-bearing ores of the Muruntau deposit. Processing of these ores is carried out by sorption technology using ion exchange resins as a sorbent. During the regeneration of saturated resin, the concomitant elements are concentrated in desorbing sulfuric acid solutions, making their extraction commercially profitable. In this connection, the solution of the issues of the associated extraction of related elements ensuring the rational use of raw materials is very relevant, while the cost of production decreases, the profit of the enterprise increases [14].

The possibility of extracting silver, copper and nickel from waste sulfuric acid solutions of the HMP-2regeneration department by cementation has been studied. The aim of the study was to determine the optimal conditions for the extraction of silver, copper and nickel from waste sulfuric acid solutions of ion exchange resin regeneration.

Several samples of waste sulfuric acid regeneration solutions were selected for the research, the composition of which according to the content of associated precious metals is presented in Table 1.

Table 1.

sulfuric acid solutions of HMP-2 regeneration

The content of associated precious metals in waste

Sample of the solution Metal concentration, mg/l

Ag Ni Cu Zn Co Pd pH

1 49,7 488 234 970 0,21 0,27 2,2

2 0,1 0,59 1,2 0,6 0,01 0,36 6,5

3 27,5 449 64,7 540 0,18 0,29 1,9

4 60,0 557 63,5 820 0,20 0,48 2,2

5 75,5 836 174 480 0,18 0,38 1,6

As can be seen from Table 1, the composition of solution No. 2 differs significantly from the composition of other solutions, both in terms of metal concentration and pH value. This is due to the fact that the sample of solution No. 2 was taken at the beginning of the process of sulfuric acid treatment of ion exchange resin. Sulfuric

acid treatment of ion exchange resin is carried out for at least 6 hours. Therefore, in order to clarify the composition of solutions from the time of resin treatment, the specialists of GMZ-2 carried out work on removing the output curve of regeneration (Fig. 1.)

№ 7 (100)

UNIVERSUM:

ТЕХНИЧЕСКИЕ НАУКИ

июль, 2022 г.

900 800 700 600 500 400 300 200

U 100

4

5

Ni Cu Zn Pd

Ag

Time of sulfuric acid treatment, h

0

6

Figure. 1. Graph of the dependence of the concentration of metals on the time of sulfuric acid treatment

From the data presented, it can be seen that during the last hour of resin regeneration, the solution is enriched with associated valuable metals to a concentration at which the extraction of these metals becomes cost-effective.

We selected solution No. 5 for the research. Studies on the extraction of associated precious metals from this solution were carried out by a cementation method using zinc dust. The research methodology was as follows. A certain volume of the test solution was placed in a thermostatically controlled reactor equipped with an electromechanical tube. The calculated amount of zinc dust was dosed into the reactor and the resulting suspension was mixed for a given time at the speed of rotation of the agitator, n = 500 rpm. At the end of mixing, the suspension was transferred to a filter (blue ribbon) and filtered under vacuum. The resulting filtrate was analyzed. In balance experiments, the sediment on the filter was washed, dried and analyzed.

Influence of zinc dust consumption. Table 2 presents data on the effect of zinc dust consumption on the completeness of metal deposition. As can be seen from the results of Table 2, the optimal from the point of view of extracting silver and copper from solutions is the consumption of zinc dust equal to 5 g/l. At the same time, the completeness of silver deposition was 99.8%, and copper 99.1%; the pH of the solution increased from 1.6 to 5.1. An increase in the consumption of zinc dust to 7.5 g / l does not lead to a significant increase in the deposition of silver and copper.

At a consumption of zinc dust of 5 g/l, the completeness of nickel deposition was only 35%. The increase in zinc dust consumption to 7.5 g/l did not significantly affect the completeness of nickel deposition, which increased by only 15% (up to 50%). At the same time, cobalt and palladium are not deposited.

Table 2.

The effect of zinc dust consumption on the completeness of metal deposition t=+20C; mixing time, t=30 min; n=500 rpm

№ Zn-dust consumption, g/l Residual concentration of metals, mg/l

Ag Ni Cu Zn Co Pd pH

1 0 75,5 836 174 480 0,18 0,38 1,6

2 0,25 45,5 796 144 540 0,18 0,38 2,8

3 1,0 19,0 730 117 650 0,18 0,38 3,9

4 2,5 9,2 664 61 2210 0,18 0,38 4,3

5 5,0 0,16 544 1,5 2400 0,17 0,38 5,1

6 7,5 0,11 414 1,5 2480 0,17 0,38 6,8

Kinetics of cementation. At the selected zinc dust consumption of 5 g/l, the kinetics of cementation of metals was studied. The results of the experiments are shown in Table 3.

№ 7 (100)

UNIVERSUM:

ТЕХНИЧЕСКИЕ НАУКИ

июль, 2022 г.

Table 3.

Kinetics of cementation of metals with zinc dust t = +20C; n= 500 rpm; consumption of zinc dust 5 g/l

№ Mixing time, min Residual concentration of metals, mg/l

Ag Ni Cu Zn Co Pd pH

1 0 75,5 836 174 480 0,18 0,38 1,6

2 5 12,2 830 15,5 1450 0,18 0,38 2,4

3 10 2,9 795 2,1 1800 0,18 0,38 4,3

4 20 0,18 685 1,7 2390 0,18 0,38 5,0

5 30 0,16 544 1,5 2400 0,17 0,38 5,1

6 40 0,15 542 1,5 2410 0,17 0,38 5,1

As can be seen from the results of Table 3, the optimal time for cementation of silver and copper is 20-30 minutes. With an increase in the cementation time to 40 minutes, the completeness of the cementation of silver and copper does not increase.

The influence of temperature. Next, the effect of temperature and consumption of zinc dust on the completeness of nickel and palladium cementation from the

iНе можете найти то, что вам нужно? Попробуйте сервис подбора литературы.

mother cells of silver and copper cementation was investigated. For this purpose, a solution was used after cementation of silver and copper, i.e. solution No. 5 (Table 2).

Data on the effect of temperature on the completeness of cementation of nickel and palladium with zinc dust are given in Table 4.

Table 4.

The effect of temperature on the completeness of carburization of nickel and palladium with zinc dust t= 30min; n= 500ob/min

Cementation temperature, C Zn-dust consumption, g/l Concentration, mg/l

Ni Pd pH

20 0 (solution after Ag and Cu deposition) 544 0,38 5,1

50 5 288 0,38 6,4

10 86 0,38 6,6

80 5 50 0,38 6,5

10 18 0,38 6,6

As can be seen from the results of Table 4, an increase in the temperature of the cementation process to +80 C with a zinc dust consumption of 10 g/ l ensures satisfactory completeness of nickel cementation (its residual concentration was 18 mg/ l). At the same time, palladium remains completely in solution.

The effect of pH. Considering that silver, as well as other metals present in the solution, are prone to hydrolysis and complexation with a change in pH, studies have

been conducted on the effect of the pH of the solution on the completeness of precipitation of silver and related metals. Neutralization of the solutions was carried out using a 24% NH4OH solution. Table 5 presents data on the effect of zinc dust consumption on the completeness of silver deposition under the condition of preliminary neutralization of the solution with ammonia to pH 9.6 (NH4OH consumption 13.6 ml/l).

Table 5.

The effect of zinc dust consumption on the completeness of Ag, Cu and Ni deposition at an initial pH of 9.6 t = +20C; mixing time, T=30min; n=500 rpm

№ Zn-dust consumption, g/l Residual concentration of metals, mg/l Note

Ag Ni Cu

1 0 75,5 836 174 The concentration of Co and Pd in the solution did not change

2 0,10 5,4 798 13,0

3 0,25 0,1 190 0,48

4 0,50 0,1 185 0,46

5 1,00 0,1 178 0,46

As can be seen from the results of Table 5, increasing the pH with NH4OH to pH 9.6 provides a significant reduction in the consumption of zinc dust: from 5 g/l (Table 2) up to 0.25 g/l. At the same time, the

residual silver content in the solution decreases from 0.16 mg/l to 0.1 mg/l.

Table 6 shows data on the effect of the initial pH on the completeness of Ag, Cu and Ni deposition at a zinc dust consumption of 0.25 g/l.

№ 7 (100)

UNIVERSUM:

ТЕХНИЧЕСКИЕ НАУКИ

июль, 2022 г.

Table 6.

Effect of the initial pH of the solution on the completeness of Ag, Cu and Ni deposition Zn-dust consumption

0.25 g/l; t=+20C; mixing time, T=30min; n=500 rpm

№ pH Residual concentration of metals, mg/l Note

Ag Ni Cu

1 1,б 25,5 б21 114 The concentration of Co and Pd in the solution did not change

2 4,0 0,12 348 1,2

3 5,2 0,10 33б 0,8

4 7,2 0,10 242 0,5б

5 8,0 0,10 190 0,5б

б 9,б 0,10 190 0,48

As can be seen from Table 6, increasing the pH of the solution with ammonia to pH 5.0 leads to almost complete precipitation of silver and copper, while nickel is deposited by 60%. The completeness of nickel deposition up to 77% can be increased by increasing the initial pH to 9.6.

Conclusions: optimal conditions for the deposition of silver from waste sulfuric acid solutions have been determined: preliminary neutralization of the solution with ammonia to pH 5 (and higher), consumption of zinc dust - 0.25 g / l; mixing time 20-30 min., ambient temperature. Under these conditions, copper and 60% nickel are also almost completely deposited.

References:

1. Strizhko L.S., Loleit S.I. Izvlechenie svetntix i blagorodntix metallov iz elektronnogo loma [Extraction of non-ferrous and precious metals from electronic scrap] // Ore and Metals. - Moscow. - 2008. - p. 160. [in Russian].

2. Sanakulov K.S. O vozmojnosti izvlecheniya blagorodntix i svetntix metallov iz otxodov obogatitelntix fabrik [On the possibility of extracting precious and non-ferrous metals from the waste of processing plants] // Mining Bulletin of Uzbekistan. - 2018. - No. 3. - pp.3-5. [in Russian].

3. Sanakulov K.S. Nauchno-texnicheskie osnovi pererabotki otxodov gorno-metallurgicheskogo proizvodstva [Scientific and technical bases of waste processing of mining and metallurgical production]. - T.: The science, 2009. -p.404. [in Russian].

4. V.N. Yaglov. Izvlechenie serebra iz otrabotannix rastvorov elektrolitov serebreniya [Extraction of silver from spent solutions of silver plating electrolytes] // Casting and Metallurgy. - 2003. - No. 2. - pp. 66-67. [in Russian].