2021. Volume 10. Issue 2 (June). Article CID e0214 DOI: 10.15275/rusomj.2021.0214_
Traumatology and Orthopedics
Original article
Designing composite external fixator for intertrochanteric fracture treatment based on Vietnamese
femur morphological parameters
Quang-Tri Le 1, Tan-Bao-An Nguyen 2
1 7A Military Hospital, Ho Chi Minh City, Vietnam 2 Ho Chi Minh City University of Medicine and Pharmacy, Ho Chi Minh City, Vietnam
Received 8 April 2021, Revised 27 May 2021, Accepted 3 June 2021
© 2021, Le Q.T., Nguyen T.B.A. © 2021, Russian Open Medical Journal
Abstract: Aim — 60 Vietnamese dry femurs were studied to design a carbon composite external fixator for intertrochanteric fracture. Its mechanical strength was evaluated.
Material and Methods — The femurs were measured by standard goniometers. The fixator injection mold was created by a CNC machine. The fixator material included carbon fiber (30 - 40% content), BT4, and PA12 plastic. The fixator strength was calculated based on the Finite Element Method.
Results — The average femoral neck-shaft angle, anteversion angle, bowing angle, head diameter, and neck width were respectively 124.850 (±7.12), 20.240 (±4.49), 14.900 (±3.27), 4.12cm (±0.30), and 3.05cm (±0.34). A mold and its resulting fixator were designed accordingly. The fixator elasticity modulus, tensile strength, Poisson ratio, and safety factor (K) were 1.32x1010 Pa, 2.21x108 Pa, 0.25, and 1.5, respectively, and max load, stress and transposition were 50-150 N, 1.21-1.38 x 108 Pa, and 0.4-1.27 mm, respectively. The composite fixator was more resistant against pressure across the x-axis but less against the y-axis than the chrome and Inox304 devices. Transposition was the smallest due to its tiny size. Load against z-axis pressure was safe for the patients.
Conclusion — This study succeeded to design a prototype carbon composite external fixator with favorable mechanical traits compared with available metal fixators. Further clinical studies are needed to achieve an accurate evaluation of its effectiveness.
Keywords: femur; morphological parameter; carbon composite; external fixator; intertrochanteric fractures.
Cite as Le QT, Nguyen TBA. Designing composite external fixator for intertrochanteric fracture treatment based on Vietnamese femur morphological parameters. Russian Open Medical Journal 2021; 10: e0214.
Correspondence to to Quang-Tri Le. Address: Department of Orthopedic, 7A Military Hospital 466 Nguyen Trai Street, Ward 8, District 5, Ho Chi Minh City 72706, Vietnam. E-mail: lqtri@ntt.edu.vn.
Introduction
Intertrochanteric fracture is a common injury in senior patients [1, 2]. It has a higher occurrence in women and people with osteoporosis [3-5]. Postmenopausal women are especially susceptible to osteoporosis due to estrogen level changes; consequently, women have a much higher intertrochanteric fracture rate than men [6-9]. Recent studies recorded higher intertrochanteric fracture instances: about 50,000 cases annually are recorded in France and 250,000 cases annually in the United States [10, 11]. An increased number of instances of this injury in senior citizens was also detected, with the rate of patients aged over 80 years augmented from 22.29% in 1977 to roughly 50% five years later [12].
Technically, intertrochanteric fracture can be healed relatively quickly due to a good level of blood supply [1, 5] with a very low rate of nonunion of femoral head necrosis (<1%); however, surgical intervention is required to prevent limb deformity and movement pain. Senior patients also suffer from prolonged bed rest complications, such as pressure ulcers, thromboembolism, or pneumonia, causing high mortality rate. Studies in Vietnam, such
as Nguyen Trung Sinh (1984) on 50 patients treated with Whitman casting, recorded poor outcomes for 40% of cases, including a 26% mortality rate within the first three months and 14% incidence of pressure ulcers. Despite the lack of comprehensive statistical data, the intertrochanteric fracture burden on the patients, their families, and society is overwhelming [8, 13].
Conservative treatments (casting or unstable methods) may lead to many complications; hence, for intertrochanteric fractures, projected internal stable bone fusion, which causes fewer or less severe complications, guarantees early rehabilitation, and reduces bed rest complications [14, 15]. Other studies employed external fixators [2, 16-22] to minimize blood loss, anesthetic risks, operation length, early weight-bearing, hospitalization time, and to ensure quick union time; their results showed satisfactory outcomes. External fixators are recommendable, for example, when surgical trauma presents a life threat [23], or for initial treatment of open intertrochanteric fracture, injuries caused by firearms, or for anatomical immobilization of the fracture site; they prevent infection, facilitate injury treatment and prepare proper conditions for further stable bone fusion.
2021. Volume 10. Issue 2 (June). Article CID e0214 DOI: 10.15275/rusomj.2021.0214_
Traumatology and Orthopedics
Prior to 1990, intertrochanteric fractures in Vietnam, despite lack of comprehensive statistics, were probably treated by traditional conservative methods, leading to many complications and a significant mortality rate [13]. From 1990 on, more advanced procedures, using intramedullary rods, dynamic hip screw plates and gamma nails, were introduced [24-28]. However, such treatments were performed mainly at large medical centers for children or senior patients without internal diseases. Fracture treatment is still affected by prolonged surgery, excessive bleeding, significant surgical trauma, the requirement of specialized equipment (such as C-Arm), and risks of nail extrusion in osteoporotic senior patients [26]. Besides, fixation nails, screws and plates in Vietnam are imported rather than manufactured domestically; hence, material supply and compatibility are significant concerns [29].
There are several studies on the implementation of the metal external fixator in Vietnam, such as by Vu Huu Dung [30], Nguyen Van Tin [31], and Le Quang Tri [4]. Recorded data were inadequate for accurate evaluation, but the outcome was encouraging. Moreover, it is possible to manufacture external fixators domestically to solve the supply issues in developing countries with limited financial resources. However, the metal fixator weight and bulkiness necessitated the use of alternative materials, amongst which carbon composites are potential candidates due to low values of their weight, heat resistance, friction and thermal expansion, making them suitable for implementation in Vietnam.
Thus, we conducted our study to design an external fixator using carbon composites suitable for Vietnam. To achieve this goal, we gathered measurement data of the proximal side of Vietnamese femurs and investigated the mechanical strength of the designed external fixator.
Material and Methods
Research objects
Bone measurements: we investigated sixty dry specimens of adult Vietnamese femurs (29 right and 31 left femurs). The femurs were randomly chosen (without gender consideration) from the specimens stored at the University of Medicine and Pharmacy at Ho Chi Minh City. The study excluded cracked, broken or defective specimens, or specimens with abnormal and pathological features, such as bone necrosis or bone tumors.
Fixator design and manufacture: crude carbon composite material.
Methods
Bone measurement. The measurements were performed by the conventional joint goniometer set (Tiger Medical, Inc.) (Figure 1). Nine morphological parameters were recorded (Table 1), each was measured three times on the same bone specimen, and the average value was computed.
Statistical methods of analysis. Skewness and kurtosis tests for normality (Sktest) were used to test the normal distribution of the data. The data group with normal distribution was analyzed using a t-test and was presented by mean ± standard deviation. The data group with a non-normal distribution was analyzed using MannWhitney test and was presented by median with lower and upper quartiles.
Data analysis was performed using STATA 10.0 and EXCEL 2007 software.
Mold and carbon composite material. Injection molding was chosen as the method for fixator manufacture. All necessary parts of the fixator were formed in just one mold since their sizes were small. The mold and the fixator were designed based on the parameters measured during the investigation of femur specimens.
i f
Figure 1. The measurement set for femur specimen investigation
Figure 2. External fixator manufacture process
Table 1. Measured parameters of the femur specimens
Parameters
Explanation
Neck-shaft angle Anteversion angle
Femoral bowing angle
Femoral head diameter Femoral neck width AB
CD
EF
HK
The angle between the femoral shaft axis and femoral neck axis The angle between the femoral neck axis and the plane going through the femoral condyles Measured from the highest point of the curve made by the femoral shaft and the horizontal plane to the midpoint of the greater
trochanter lateral facet and lateral side of the lateral condyle The diameter of the greatest circumference of the femoral head The diameter of the greatest circumference of the femoral neck Located on the tangent line of the femoral neck superior surface; it goes through the lower ridge of the greater trochanter Located on the tangent line of the femoral neck superior surface; it crosses the d line and point D. The d line goes through the lower ridge of the lesser trochanter and is perpendicular to the femoral shaft axis The EF line is parallel with AB and CD lines, it crosses the midpoint of the femoral neck width H is the highest point of the bow formed by the femoral shaft and the horizontal plane, and K is located on the lower ridge of the
greater trochanter
2021. Volume 10. Issue 2 (June). Article CID e0214 DOI: 10.15275/rusomj.2021.0214_
Traumatology and Orthopedics
Table 2. Bone measurements
Parameters N Average* SE* Min* Max* p-value
Left 29 125.79 6.35 115.00 135.00
Neck-shaft angle Right 31 123.97 7.75 103.00 138.00 0.320
Total 60 124.85 7.12 103.00 138.00
Left 29 20.51 4.49 15.00 30.00
Anteversion angle Right 31 20.77 4.77 10.00 30.00 0.650
Total 60 20.24 4.24 10.00 30.00
Left 29 14.55 3.06 10.00 20.00
Bowing angle Right 31 15.22 3.48 10.00 30.00 0.650
Total 60 14.90 3.27 10.00 30.00
Left 29 4.07 0.28 3.50 4.60
Femoral head diameter Right 31 4.17 0.32 3.50 4.80 0.170
Total 60 4.12 0.30 3.50 4.80
Left 29 2.96 0.32 2.20 3.60
Femoral neck width Right 31 3.14 0.35 2.60 3.84 0.080
Total 60 3.05 0.34 2.20 3.84
Left 29 8.02 0.42 6.80 8.70
AB Right 31 8.30 0.52 7.40 9.80 0.390
Total 60 8.12 0.75 6.80 9.80
Left 29 8.80 0.61 7.30 10.0
CD Right 31 9.06 0.68 7.80 10.3 0.140
Total 60 8.90 0.65 7.30 10.3
Left 29 8.51 0.50 7.10 9.50
EF Right 31 9.03 0.53 7.90 9.90 0.220
Total 60 8.70 0.52 7.10 9.90
Left 29 14.50 1.15 11.50 16.50
HK Right 31 14.89 1.29 13.00 17.00 0.210
Total 60 14.70 1.23 11.50 17.00
* - the measurement unit was degree (0) for the angles and cm for other parameters
o
Figure 3. Design of the mold and injection molding machine. (1) Screw motor; (2) Screw; (3) Material hopper; (4) Barrel; (5) Heater bands; (6) Injection chamber; (7) Nozzle; (8) Mold (consists of two halves); (9) Ejected product
The mold was made from CT45 steel, which is resistant to erosion and oxidation, has a high load carrying capacity, melting point and elasticity. The mold consisted of an upper half and a lower half, and comprised automatic ejectors. The mold parts were processed by a CNC machine and were plated.
The composite material was made from a mixture of carbon fiber (HITCO, U.S.), BT4 (NIIGRAFIT, Russia), and polyamide 12 (PA12) plastic pellets, with a 30 - 40 % fraction of a carbon fiber. The mixture was then processed to make the composite PA12-carbon pellets. The material pellets were then forced into the molding machine to form the desirable parts. The operating temperatures were 250-260oC. The manufacture process is presented in Figure 2.
The designed fixator was investigated for mechanical strength and was compared with available imported fixators. Mechanical
strength was calculated based on the Finite Element Method (FEM) [32, 33] using the ANSYS® 13 software. The testing models were built by specialized CAD software. The structure was modeled three-dimensional, and the solid element was used. The mechanical strength was tested against the pressure across the x-axis (i.e., across the fixator main axis), y-axis, and z-axis (perpendicular to the fixator plane).
Data analysis. The data were processed by STATA 12.0, using appropriate algorithms.
Results
Recorded measurements of Vietnamese femur specimens (N=60)
The average recorded neck-shaft angle was 124.850 (±7.12). The corresponding values of anteversion angle, bowing angle, femoral head diameter and femoral neck width were 20.240 (±4.24), 14.900 (±3.27), 4.12 cm (±0.3 cm), and 3.05 cm (±0.34 cm), respectively. The corresponding average measurements of AB, CD, EF, and HK were 8.12 cm (±0.75 cm), 8.90 cm (±0.65 cm), 8.70 cm (±0.52 cm), and 14.70 cm (±1.23 cm), respectively. There was no significant difference between the left and right femurs (p>0.05, a=0.95). There was just one specimen with a neck width lower than 2.50 cm (1.67%). The detailed measurements are presented in Table 2.
Mold and external fixator designs
Injection molding was chosen as the method for fixator manufacture and was described in the Materials and Methods section. The mold design was based on the measurements of the femur specimens and is shown in Figure 3.
2021. Volume 10. Issue 2 (June). Article CID e0214 DOI: 10.15275/rusomj.2021.0214_
Traumatology and Orthopedics
Figure 4. Design of the external fixator. (1) and (2): femoral neck nails, (3) and (4): femoral shaft nails, (5) and (6): anterior and posterior halves of the cylinder, (7) and (8): anterior and posterior halves of the prism, (9): connecting joint between the two parts of the fixator, (10): cross-section separating the prism halves forming a 15 angle with the coronal plane top-down and back-to-front, (11): halves of fixation rods.
Figure 5. Lateral side and medial side of the external fixator prototype with inserted screws.
The fixator design is presented in Figure 4, and a prototype is shown in Figure 5. The fixator consists of two parts. The bone nails at the proximal femur part were clamped in the ditches between two halves of a cylindrical part used for both left and right limbs. The front half (to the front from the coronal plane) could slide along the ridge to the appropriate ditch of the back half, and the angle between this sliding plane and the screw plane was 200, similar to the femoral anteversion angle. Two halves of a rectangular prism kept the nails at the femur distal part. The coronal plane angle with the prism halves' contact surface was 150, similar to the anterior protrusion.
Mechanical strength of the designed composite external fixator
The following composite fixator parameters were measured and recorded: the elasticity modulus, tensile strength, Poisson ratio, and safety factor (K) were 1.32x1010 Pa, 2.21x108 Pa, 0.25, and 1.5, respectively. Table 3 presents several mechanical strength
parameters of investigated fixators vs. other available imported external fixator (for comparison).
Discussion
Vietnamese femur measurements
The measurements were performed on 60 randomly selected Vietnamese femur specimens (29 of the right femur or 48.33%; and 31 of the left femur bone, or 51.76%). The measured parameters were not significantly different among the right and left femurs (p<0.05), which was similar to other domestic and foreign studies, such as the research by Nguyen Van Tin [8], or the report by Trinkaus and Anderson (1998) [34]; both asserted an insignificant difference among the legs. The measurements on CT scan images by Baharuddin and colleagues [35] showed an insignificant difference between left and right femurs, but a significant difference between males and females, which could hardly be investigated on dry bone specimen, like those in our study.
The value of the neck-shaft angle is high in infants (on average, 150-1600), then it decreases during the body growth, reaching 1350 in adults. This value has been used as a reference for the manufacture of femoral surgical equipment. The neck-shaft angle is a significant parameter for treatment, using a dynamic hip screw or dynamic condylar screw fixators; these surgeries usually require an angle value of 1350 [36]. However, this condition does not seem to fit Vietnamese people, since our study recorded a smaller neck-shaft angle (1240 for the left side and 1260 for the right side).
Medical publications mention various anteversion angle measurements, including measurements on dry bone specimens; however, it is more convenient to use image materials, such as radiographic, ultrasonic, CT, or MRI images. The measurements on dry femur specimens were affected, for example, by difficulties in identification of the fovea, or the midpoint on the femoral neck outer surface. The comparison of measurements on dry bones vs. image materials was performed by Aamodt et al. [37]. In our study, the average anteversion angle on dry bones was 20.24 ± 4.240, within the acceptable range reported in published sources. Another study in India by Rokade and Mane (2009) [38] reported a quite different value (18.68±6.37). This was probably caused by the difficulties and high subjectivity of these parameter measurements, resulting in a significant difference.
Femoral head diameter and femoral neck width were also important parameters for the suitable design of surgical materials. Our study recorded the value of 4.12±0.3 cm and 3.05±0.34 cm, respectively. The recorded Vietnamese femoral head diameter was quite similar to the parameters of Malaysians but somewhat smaller than those of Europeans and Americans; meanwhile, just a slight difference was found in femoral neck width.
Table 3. Mechanical strength values of carbon composite, chrome, and Inox external fixators
Types of external fixators Pressure across the x-axis Pressure across the z-axis Pressure across the y-axis
Max. load (N) 50 150 90
Carbon composite Max. stress (Pa) 1.38x108 1.21x108 1.37x108
Max. transposition (mm) 1.27 0.4 0.69
Max. load (N) 32 140 120
Chrome Max. stress (Pa) 1.32x108 1.4x108 1.37x108
Max. transposition (mm) 2.3 1.76 19
Max. load (N) 50 45 100
Inox304 Max. stress (Pa) 1.37x108 1.31x108 1.4x108
Max. transposition (mm) 2.49 1.25 0.55
2021. Volume 10. Issue 2 (June). Article CID e0214 DOI: 10.15275/rusomj.2021.0214_
Traumatology and Orthopedics
Figure 6 Proposed model for the external fixator and bone nail positions.
(1) The Schanz nail tip is 10 mm from the head cartilage, (2) the distance between two femoral nails is 20-25mm, and (3) the nails are 2.5-5 mm from the superior and inferior surfaces of the neck. Hence the length of nails submerged inside the bones should be AB=80-10=70 mm and CD=90-10=80 mm.
Bowing angle is rarely referred to in studies, despite its importance in equipment manufacturing. Our studies recorded a value of 14.90 (±3.27), which fitted in the range of 10°-15° in Gray's Anatomy.
The lengths of AB, CD, and EF are critically important for treating intertrochanteric fracture using external fixator and surgical nails. Our study established AB=8.12±0.75 cm, CD=8.9±0.65 cm, EF=8.7±0.52 cm, and HK=14.7±1.23 cm. AB, CD, and EF measurements fell within the range of 8-9 cm, and were smaller than in other studies, such as by Pires and colleagues (Brazil) [39]. The latter research yielded the value of 8.6-9.4 cm; it was probably due to the fact that the study was based on image materials rather than dry bones.
External fixator design
The recorded data showed that the mechanical strength against the stress applied across the z-axis of the carbon composite fixator was similar to the chrome and Inox304 devices. The mechanical strength against the stress across the x-axis, the carbon composite fixator performed better than the other two and yielded a smaller transposition. However, it performed worse against the stress applied across the y-axis. The composite fixator was small in size; hence, its bending transposition was smaller than i larger fixators, providing better bone fixation. Its maximum load against z-axis pressure was 50 N (~5.1 kg), which guaranteed patient safety.
Most of the studies suggested that, for femoral head blood vessel safety, the femoral nails were 10 mm apart from the femoral head cartilage and 2.5-5 mm apart from the femoral neck superior surface. Our study demonstrated that the average distance between the superior and inferior neck surfaces was 30 mm. With these data, our study proposed a model for nail positioning, presented in Figure 6.
The external fixator design must fit the proximal Vietnamese size of a femur and guarantee stable fixation with a proper union and no malalignment. The femoral nails had to be inserted into the neck and shaft, and attention had to be paid to the factors that contributed to the biomechanics of the intertrochanteric region, including 200 anteversion angle of the femoral neck, the anterior protrusion of the femur upper third, and the coronal plane of the shaft.
Conclusion
Based on the measurement of nine morphological parameters of proximal end of the Vietnamese femur, this study succeeded to design a prototype external fixator using carbon composite as material for treating intertrochanteric fracture for Vietnamese patients. Its mechanical strength was comparable to available chrome and Inox external fixators while the transposition was the smallest, which was favorable, and its load against z-axis pressure was safe for the patients. Further clinical studies are required to achieve an accurate evaluation of its treatment effectiveness for intertrochanteric fractures.
Acknowledgements
We thank our colleagues from the Ministry of Defense, 7A Military Hospital, and the University of Medicine and Pharmacy at Ho Chi Minh City, who provided support and facilities, which were very helpful for our research.
Conflict of interest
The authors declare that they have no conflict of interest.
1.
References
Guyton JL. Fractures of Hip, Acetabulum and Pelvis. In: Canale ST,
Campbell WC, Eds. Campbell's Operative Orthopaedics, 9th ed. St. Louis: Mosby. 1998: 2181-2276.
2. Zayda AI, Zaki EM, Marei S. Ilizarov Fixator in treatment of intertrochanteric fracture femur in geriatric high-risk patients. Biomed J Sci Tech Res. 2018; 2(1): 2325-2358. https://doi.org/10.26717/BJSTR.2018.2.000688.
3. Bejui JB. Ostéosynthése des fractures trochanteriennes. In:
Conf oeernsesrd ' etí?eígrrejTie994d e la SOFCOT
46: 1-18. French.
4. Le QT. Treatment of intertrochanteric fractures in senior patients by external fixator under light enhancing monitor. In: Reports in XV annual conference, 2008: 298-309. Vietnamese.
5. Nguyen TS, Nguyen DP, Nguyen XT, Ngu VT. Orthopedics. Hanoi: Medical Publishing House. 2004: 390-394.
6. Ji MX, Yu Q. Primary osteoporosis in postmenopausal women. Chronic Dis Transi Med 2015; 1(1): 9-13. https://doi.org/10.1016/Lcdtm.2015.02.006.
7. Nasab SAM, Khorramdin E. The assessment of mortality and quality of life after intertrochanteric fracture of femur in patients older than 60 at Emam Khomeini Hospital of Ahvaz. Pak J Med Sci 2017; 33(4): 895898. https://doi.org/10.12669/pjms.334.13146.
8. Nguyen VT. Treatment of femoral neck and intertrochanteric fractures by external fixator. HCMCJ Med 2003; 292: 151-261. Vietnamese.
9. Tran DT. Osteoporosis in Older People. Hanoi: Medical Publishing House. 1999: 7-55. Vietnamese.
10. Scheerlinck T, Haentjens P. Fractures de l'extrémité supérieure du fémur chez l'adulte. In: Encycl Méd Chir (Editions Scientifiques et Médicales), Appareil Locomoteur. Paris: Elsevier SAS. 2003: 14-075-A-10. French. http://ekladata.com/gABI 3t4aGxPVj JRm-qOsWqbWg/Fractures-de-l-extremite-superieure-du-femur-chez-l-adulte.pdf.
11. Lorich DG, Geller DS, Nielson JH. Osteoporotic Pertrochanteric Hip Fractures: Management and Current Controversies. Instr Course Lect. 2004; 53: 441-544. https://pubmed.ncbi.nlm.nih.gov/15116633.
12. Hornby R, Evans JG, Vardon V. Operative or conservative treatment for trochanteric fractures of the femur. A randomised epidemiological trial in elderly patients. J Bone Joint Surg Br 1989; 71(4): 619-623. https://doi.org/10.1302/0301-620x.71b4.2670950.
2021. Volume 10. Issue 2 (June). Article CID e0214 DOI: 10.15275/rusomj.2021.0214_
Traumatology and Orthopedics
13. Nguyen TS. Rehabilitation results of senior intertrochanteric fracture patients. J Surg. 1984; 10: 118-121. Vietnamese.
14. LaVelle DG. Fractures of Dislocation of the Hip. In: Campbell WC, Canale ST, Beaty JH, eds. Campbell's Operative Orthopaedics. 11th Ed. Pennsylvania: Mosby/Elsevier. 2008: 3239-3262. https://www.worldcat.org/title/campbells-operative-
orthopa edics/oclc/70929249.
15. Capozzi JD, Levy RN, Mont MA. Intertrochanteric Hip Fractures. In: Browner BD, Jupiter JB, Levine AM, Trafton PG, eds. Skeletal Trauma: Fractures, Dislocations, Ligamentous Injuries. 1st ed. Philadelphia: WB Saunders Company. 1992: 1443-1484.
16. Ahmed AR. An innovative external fixator for the management of trochanteric fractures of the femur. Egypt Orthop J 2014; 49(1): 1-5. https://doi.org/10.4103/1110-1148.140522.
17. Vossinakis IC, Badras LS. Management of pertrochanteric fractures in high-risk patients with an external fixation. Int Orthop 2001; 25(4): 219-222. https://doi.org/10.1007/s002640100238.
18. Tomak Y, Kocaoglu M, Piskin A, Yildiz C, Gulman B, Tomak L. Treatment of intertrochanteric fractures in geriatric patients with a modified external fixator. Injury 2005; 36(5): 635-643. https://doi.org/10.1016/Mniury.2004.10.013.
19. Moroni A, Faldini C, Pegreffi F, Hoang-Kim A, Vannini F, Giannini S. Dynamic hip screw compared with external fixation for treatment of osteoporotic pertrochanteric fractures. A prospective, randomized study. J Bone Joint Surg Am 2005; 87(4): 753-759. https://doi.org/10.2106/ibis.d.01789.
20. Mussa MA, Ahmed AR. External fixation of trochanteric fractures of the femur. J Orthoplastic Surg 2019; 3(1): 74-80. https://iournaloforthoplasticsurgery.com/index.php/JOPS/article/view /48 to
21. Vekris MD, Lykissas MG, Manoudis G, Mavrodontidis AN, Papageorgiou CD, Korompilias AV, et al. Proximal screws placement in intertrochanteric fractures treated with external fixation: Comparison of two different techniques. J Orthop Surg Res 2011; 6: 48. https://doi.org/10.1186/1749-799x-6-48.
22. Wang ZP, Liu L, Xue W, Zhou HR, Song YX, Cai LY, et al. Curative effect analysis on closed reduction and external fixator under local anesthesia for the treatment of intertrochanteric fracture in elderly patients with high-risk. Zhongguo Gu Shang 2016; 29(6): 502-504. Chinese. https://pubmed.ncbi.nlm.nih.gov/27534078/.
23. Mitkovic M, Milenkovic S, Radenkovic M, Mladenovic D, Golubovic Z, Stanojlovic M. Surgical treatment of the trochanteric fractures by using the external and internal fixation methods. FU Med Biol 2003; 10(2): 79-83. http://facta.iunis.ni.ac.rs/mab/mab200302/mab200302-05.pdf.
24. Mai DD, Le VB, Nguyen TA, Pham Ngoc TA. Preliminary results of intertrochanteric fracture treatment by gamma nails in Thai Nguyen Central General Hospital. J Sci Technol 2014; 118(04): 145-151. Vietnamese.
25. Nguyen HN. Treatment of adult closed intertrochanteric fractures in Viet Duc Hospital - Hanoi. J Surg 2000; 1: 40-43. Vietnamese.
26. Nguyen TB, Nguyen VT, Luu HH, Le HH. Treatment of closed intertrochanteric fractures in senior patients by closed bone fusion using Ender intramedullary rod. Vietnam J Med 2003; Special Issue: 6468. Vietnamese.
27. Pham CL. Intertrochanteric fracture treatment of 70 cases. J HCMC Gen Med 1997; 2(3): 66-70. Vietnamese.
28. Nguyen PN. Intertrochanteric fracture treatment by DHS bone fusion in Ba Ria Hospital. J News Sci Technol Ba Ria Vung Tau 2019; 3: 6-9. Vietnamese.
29. Luong DL. Locking plate for intertrochanteric fracture treatment in senior patient. In: Summary record of the XVI Orthopedics Conference. 2009: 131-136. Vietnamese.
30. Vu HD, Ly TK. Evaluation of intertrochanteric fracture treatment on senior patients using side external fixator. Vietnam J Med 2003; Special Issue: 144-147. Vietnamese.
31. Nguyen VT, Nguyen TB. Treatment of femoral neck and intertrochanteric fractures by external fixator (compressive clockwise and anti-clockwise thread rod). Vietnam J Med 2003; 292: 157-160. Vietnamese.
32. Disegi J. Implant Material: Unalloyed Titanium. 6th Ed. West Chester, PA: Synthes. 2008; 26 p. https://docplayer.net/19907213-Sixth-edition-implant-materials-unalloyed-titanium.html.
33. Zienkiewicz OC, Taylor RL. The Finite Element Method for Solid and Structural Mechanics. 7th Ed. Oxford: Butterworth-Heinermann. 2013; 672 p. https://www.elsevier.com/books/the-finite-element-method-for-solid-and-structural-mechanics/zienkiewicz/978-1-85617-634-7.
34. Anderson JY, Trinkaus E. Patterns of sexual, bilateral and interpopulational variation in human femoral neck-shaft angles. J Anat 1998; 192 (Pt 2)(Pt 2): 279-285. https://doi.org/10.1046/L1469-7580.1998.19220279.x.
35. Baharuddin MY, Kadir MRA, Zulkifly AH. Morphology study of the proximal femur in Malay population. Int J Morphol 2011; 29(4): 13211325. https://doi.org/10.4067/S0717-95022011000400042.
36. Pauwels F. Biomechanics of the Locomotor Apparatus. Berlin: SpringerVerlag. 1980; VIII, 520 p. https://doi.org/10.1007/978-3-642-67138-8.
37. Aamodt A, Teriesen T, Eine J, Kvistad KA. Femoral anteversion measured by ultrasound and CT: A comparative study. Skeletal Radiol 1995; 24(2): 105-109. https://doi.org/10.1007/bf00198071.
38. Rokade S, Mane AK. Femoral anteversion: Comparison by two methods. Internet J Biol Anthropol 2009: 3(1): 1-6. https://ispub.com/IJ BA/3/1/8728.
39. Pires RE, Prata EF, Gibram AV, Santos LE, Lourengo PR, Belloti JC. Radiographic anatomy of the proximal femur: Correlation with the occurrence of fractures. Acta Ortop Bras 2012; 20(2): 79-83. https://doi.org/10.1590/s1413-78522012000200004.
Authors:
Quang-Tri Le - MD, PhD, Director, Department of Orthopedics, 7A Military Hospital, Ho Chi Minh City, Vietnam. https://orcid.org/0000-0002-2777-0828.
Tan-Bao-An Nguyen - MD, MSc, Lecturer, Department of Plastic and Cosmetic Surgery, Faculty of Medicine, Ho Chi Minh City University of Medicine and Pharmacy, Ho Chi Minh City, Vietnam. https://orcid.org/0000-0002-3090-2262.